Bullseye Rods - Copper Green Lustre - 4-6mm - Transparent

As 1717 is heated into a gather and wound onto a mandrel, it will opalize on the rod between the gather and the cold glass. If formed hot enough, the bead will remain transparent. When you are ready to develop a metallic sheen, the glass should be relatively cool (no visible heat) and stable on the mandrel. Create a reduction atmosphere by turning the propane (fuel) up and while passing the bead through the flame, watch for the surface of the glass to become metallic. The lustre surface develops readily on cooler glass and can vary greatly depending on the length of time spent in the reduction atmosphere. Once this has happened, the piece should be put into an annealing kiln. This is a finishing step. If the metallic surface is reintroduced to a neutral flame, it will dissipate. It can be brought out again by returning it to a reduction atmosphere.

Often a design will necessitate holding the glass at a warm, stable state (cooler than molten, fluid glass). Under these conditions, 1717 is likely to opalize. Once opalized, 1717 may still be reduced as described above to bring out a metallic sheen, though it takes a little longer to develop. The finished appearance is different because it is backed by the opalized glass. Consider using 1717 for its unique opalized color and work with it in a neutral to oxidizing atmosphere without reduction treatment.

When molten, this glass has a low viscosity, and can be quite soft, which may result in a blurred edge where it meets other glasses. In addition, the process of reducing the glass can cause a metallic sheen over areas of glass immediately adjacent to this style.